Magnetherstellungsprozess

Sintering Process of Magnets

First:Melting
The materials are exposed to mid frequency and melted in an induction furnace.

Zweite:Jet Milling
After completion of various process steps, die Barren werden zu Partikeln mit einer Größe von mehreren Mikrometern pulverisiert. Um Oxidation zu verhindern, die kleinen Partikel werden durch Stickstoff geschützt.

Dritte:Drücken
The magnetic particles are placed in a jig and a magnetic field is applied while the magnets are pressed into shape. Through this process, we achieve magnetic anisotropy.

Fourth:Sintering
The magnetic particles are placed iIngots that have been pressed are heat treated in a sintering furnace. The density of the ingots prior to sintering is about 50% of true density but after sintering, the true density is 100%. Through this process the ingots’ measurement shrink by about 70%-80% and their volume is reduced by about 50%. Aging the magnets after sintering adjusts the properties of the metals.n a jig and a magnetic field is applied while the magnets are pressed into shape. Through this process, we achieve magnetic anisotropy.

Fifth:Inspection
Basic magnetic properties are set after the sintering and aging processes are complete. Key measurements including remnant flux density, coercivity, and maximum energy product are recorded.Only those magnets that pass the inspection are sent to subsequent processes including machining and assembly

Sixth:Cutting

Seventh:Machining
Due to shrinkage from the sintering process, required measurements are achieved by grinding the magnets withabrasives. Diamond abrasives are used for thisprocess because the magnet is very hard.
Eighth:Überzug
To best suit the environment in which they will be used, the magnets are subject to various surface treatments. Nd-Fe-B magnets are generally susceptible to rust so they are surface treated with nickel or paint.

Ninth:Size testing
Magnets that have been machined and plated are measured and visually inspected.To ensure the high precision,we have totest the size in order to control the tolerance.So far our normal tolerance reaches 0.03

Tenth:Magnetisierung
Magnets that have been machined and plated are measured and visually inspected. In Ergänzung, magnetic properties, corrosion and maximum energy are tested to specifications.
 

Eleventh:Packing
Magnets that have passed product testing are packaged and shipped. Flux leakage shields are utilized for air shipment when required. Magnet products are shipped to worldwide customer manufacturing locations